The invention relates to a ceramic tile with high stain resistant performance. According to weight percentage, the materials of the ceramic tile are that: 25 to 75 percent of SiO2, 15 to 23 percent of Al2O3, 3 to 16 percent of K2O +Na2O3, 0.5 to 1.5 percent of Fe2O3+TiO2, 5 to 30 percent of MgO and 0 to 10 percent of CaO; the preparation processes are that: ore selecting - material feeding - homogenizing chamber - using chamber - testing - proportioning - ball milling - screening for eliminating iron - slurry stale homogenizing - spray drying - staling in a chamber - punch forming - drying - printing - sintering temperature - polishing - testing - packaging - entering storehouse- dispatching; the fineness of ball-milling glaze slip is that 0.8 to 1.2 percent of 320 meshes; 0.15 to 0.55 percent of 325 meshes; the sintering temperature is from 1050 to 1225 DEG C, the sintering period is 80 to 90 minutes; the water absorption rate of the product is less than or equal to 0.03 to 0.05 percent, and the stress resistance capacity is larger than or equal to 45MPa with good stain resistance effect.